|Place of Origin:||Shanghai China (Mainland)||Classification:||Double Components Adhesives||Main Raw Material:||Epoxy|
|Usage:||Construction,Electronics||Brand Name:||Jorle||Model Number:||ZR1507|
|Mixed viscosity:||1000-2000 mPas(25°C)||Mixture density:||1.10 g/cm3(25°C)||operation time:||120 min 25℃|
|curing time:||80/1.5 or 25/24 ℃/hr||hardness:||50 Shore A||glass transition temperature:||>20 kV/mm(25°C)|
|expansion coefficient:||44 μm/(m,℃)||water absorption:||<0.1 24h 25℃ %||dielectric strength:||0.014 (1MHz)(25°C)|
|Loss factor:||3.53 (1MHz)(25℃)|
|Packaging Detail:||Agent A 10kg,Agent B 10kg We can also packing Avoid Water Ideal Sealant For Connector as your requirement.|
|Delivery Detail:||Within 25-30 days upon receipt of your L/C or 30% deposit|
Avoid Water Ideal Sealant For Connector is one of our most popular products.Against moisture, dirt, atmosphere......
ZR1507 Avoid Water Ideal Sealant For Connector is a room temperature/heating curing epoxy resin glue. ZR1507 is used for design, protection of the potting need high strength or confidential electronic products.
ZR1507 Flexible epoxy potting glue without heating can cure. 3:1 (weight ratio) completely mixed part A and part B, form protection in a period of curing time.
After curing glue has the following characteristics:
Against moisture, dirt and other atmospheric composition
Has confidential role
No solvents, no cure by-products
Have stable mechanical and electrical properties between -45°C-120°C
80/1.5 or 25/24
Operation time is a quantity of cement with 100 g.
A, B two components in proportion to remove mixing ratio, mixing, vacuum suction bubble in operation period, remove the potting products to casting, such as potting product is too big, suggest points potting, then according to The Times curing(80°C/90min or 25°C/10hr)
Agent A place for a long time, maybe produce precipitation, mix part A and B access should be paid attention to save after sealing.
Mixing should pay attention to the same direction, otherwise, it will stir with too much bubble; Borders and the bottom of the container sizing material should also stir well, can appear otherwise stir caused by uneven local not curing phenomenon.
Casting the product vacuum pumping, remove again bubble can improve after curing products comprehensive performance.
Temperature is too low will lead to curing speed partial slow, heat cure advice; Potting thickness more than 2 cm above 80 °C not directly in the curing, lest cause explosive together.
This glue curing exothermic reaction, match the process as the quantity of cement can affect the operation, so the length of time with 100 g resin content of operation time is only a reference time.
glass transition temperature
Remark:All the above data come from 25 °C and 55% RH glue curing conditions after 7 days.
Agent A 10kg,Agent B 10kg
Storage and transportation:
Part A and part B need to avoid light, heat, save after sealed. (Can be used as the non-dangerous goods transport and storage)
Shelf life Agent A: 1 year, Agent B: 6 months(25°C).