|Place of Origin:||Shanghai China (Mainland)||Classification:||Double Components Adhesives||Main Raw Material:||Epoxy|
|Usage:||Construction,Electronics||Brand Name:||Jorle||Model Number:||ZR112|
|Mixed viscosity:||1000-2000||Mixture density:||1.45||Gel time:||40 min 25℃|
|curing time:||80/1.5 or 25/10 ℃/hr||hardness:||80 Shore D||conductivity factor:||0.4 W/mK|
|expansion coefficient:||44 μm/(m,℃)||water absorption:||<0.1 24h 25℃ %||dielectric strength:||>20 kV/mm 25℃|
|Loss factor:||0.014 (1MHz)(25℃)|
|Packaging Detail:||25 kg /set; 5kg / set; 1kg/ set We can also packing Avoid-knock Anti-flame Glue For Television as your requirement.|
|Delivery Detail:||Within 25-30 days upon receipt of your L/C or 30% deposit|
Avoid-knock Anti-flame Glue For Television is one of our most popular products.Against moisture, dirt and other atmospheric...
ZR112 Avoid-knock Anti-flame Glue For Television is a room temperature/heating curing epoxy resin glue. ZR112 is used for design, protection of the potting need high strength or confidential electronic products.
ZR112 epoxy potting materials without heating can cure. 4:1 (weight ratio) completely mixed part A and part B, form protection in a period of curing time.
After curing glue has the following characteristics:
Against moisture, dirt and other atmospheric composition
Has confidential role
Solvents, no cure by-products
Have stable mechanical and electrical properties between -45°C-120°C
black viscous liquid
80/1.5 or 25/10
Operation time is a quantity of cement with 100 g.
A, B two components in proportion to remove mixing ratio, mixing, vacuum suction bubble in operation period, remove the potting products to casting, such as potting product is too big, suggest points potting, then according to The Times curing(80°C/90min or 25°C/10hr)
Agent A place for a long time, maybe produce precipitation, mix part A and B access should be paid attention to save after sealing.
Mixing should pay attention to the same direction, otherwise, it will stir with too much bubble; Borders and the bottom of the container sizing material should also stir well, can appear otherwise stir caused by uneven local not curing phenomenon.
Casting the product vacuum pumping, remove again bubble can improve after curing products comprehensive performance.
Temperature is too low will lead to curing speed partial slow, heat cure advice; Potting thickness more than 2 cm above 80 °C not directly in the curing, lest cause explosive together.
This glue curing exothermic reaction, match the process as the quantity of cement can affect the operation, so the length of time with 100 g resin content of operation time is only a reference time.
flame retardant rating
Remark:All the above data come from 25 °C and 55% RH glue curing conditions after 7 days.
25 kg /set; 5kg / set; 1kg/ set
Storage and transportation:
Part A and part B need to avoid light, heat, save after sealed. (Can be used as the non-dangerous goods transport and storage)
Shelf life Agent A: 1 year, Agent B: 6 months(25°C)