The ultimate success of the casting design depends on the communication between the designer and foundry engineers. When the foundry is properly informed of part requirements, there is usually a compromise of specifications that will allow for maximum compliance to print specifications and finish part design.
1 Standard Linear Tolerance(mm)
As-cast tolerances of angles is mainly a function of the part design and their ocation in casting. They range from +/- 1/2 degree (considered minimum) for well supported positions to +/- 2 degree where existing distortion could be expected. Inclusion of gussets and ribs normally minimizes distortion and many sections can be mechanically straightened.
2 Flatness, Strengteness and Roundness
Possible Thickness Section Sink per Face of Casting
Up to 25
25 to 50
50 to 100
100 to 150
Straightening adds cost, but sometimes cannot be avoided. The actual straightening costs are often dependent on the tightness of the tolerance specified, so do not specify tighter flatness, straightness, roundness, or other requirements than you actually require. (WOTECH typically straightens parts using die sets that will be included in your tooling price.)
3 Size and Weight Range Size and Weight. Part size and weight are the most critical factors in determining part cost because mold capacity is limited by both size and weight. The more pieces that can run on a mold, the lower the part cost. Unnecessary mass should always be removed by correct engineering practices to reduce part weight.
up to 100
0.10 to 1.50
Min. Wall Thickness
5 to 105 Surface Roughness
80 to 120 RMS are average.
4 Hole Length
Making a good hole in a casting is dependent on the integrity of the shell. The ratio of holediameter to length is important in determining what can be offered. Blind holes must have aradius at the top and the bottom of the hole to insure that a strong core is built for castingpurposes and to insure the best possible casting.
5 Heat Treatment Heat treatments are used to control hardness, mechanical properties, corrosion resistance, and surface treatments. Unless otherwise indicated, all alloy steels are quoted with a normalize or anneal. All 300 series stainless steels and 17-4PH are quoted with a solution anneal. 6 Pictures of investment casting parts
If you are interested in our goods, Please contact Emily feel free.
We can produce all kinds of mechanical parts and components based on technical drawing,sample,or even a Concept.
Our Competitive advantages: One-Stop Shopping from "Drawing to Part".
More than 10 years' experience in domestic and overseas markets makes us a professional and efficient company in the industry.We have been keeping stable business relations for more than 5 to 10 years with our major clients in Europe and US market,and Asia.