1. One component thread locker sealant glue
2. Use in -50--200 degree
3. 24 hours curing
4. MSDS and ISO9001
Senior Member of Shanghai International Chamber of Commerce
Uncured Testing Term Testing Standard Typical Value Range Appearance(uncured) White Paste Chemical Type Methacrylate Ester Viscosity(mPa.s) GB/T2794-1995 Brookfield RVF 3#rotor 2 rpm 550000 280,000-800,000 Density( g/cm 3 ) GB/T 13354-1992 1.15 Flash Point( °C ) SH/T0733-2004 >93 Maximum thread diameter M80 Fixed Time(h) <1 Fully Cured Fully cured at RTV(h) 24 Maximum sealing pressure(MPa) 71.0 Strength for remove Medium Sealing pressure of work time Instant Operation Temperature -50-200
% of Initial Strength Environment °C 100 hr 500 hr 1000 hr Motor Oil 40 100 100 100 Unleaded Gasoline 22 90 80 80 Ethanol 22 85 85 85 Acetone 22 75 70 60 Water/Glycol 87 100 75 75
A6567 , is one component, requires no mixing, low strength anaerobic thread sealant.It is designed for the locking and sealing of metal tapered threads and fittings. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration .
Features 1. One component, requires no mixing 2. Low intensity, high lubricating properties,cured fast. 3. No pollution to the system, good resistance to shock and vibration. 4. Removed by hand-operated tool. 5. Resistant to elevated temperature up to 200°C
Professions involved 1.Instant sealing of metal tapered threads up to M80(NPT) 2.Sealing and locking of tapered/straight thread and stainless steel. 3.Prevent the thread corrosion.
1.With plastic tube packing, it is easy to glue. Cleaning the component interface before the
2.Increasing 20% removal of torque, removed easily.
3.Excess adhesive solution won’t cure, can be wiped with a cloth.
4.Used as a sealant, the pressure test can be done instantly after the gluing.
5.If the pipeline need to bear high pressure, high shock or strong vibration, then do the test after 24
hours’ fully cured.