Glass Compound Adhesive,SK-1698 glue for stone,epoxy resin adhesive

FOB Reference Price:Get Latest Price
US $5-10 / Piece | 10000 Piece/Pieces (Min. Order)
Supply Ability:
500 Carton/Cartons per Week
Port:
Changsha
Report Suspicious Activity
Overview
Quick Details
Place of Origin:
Hunan, China (Mainland)
Classification:
Volatile Solvent Adhesives
Main Raw Material:
Epoxy
Usage:
Construction, Fiber & Garment, Footwear & Leather, Packing, Transportation, Woodworking, bonfing bewteen precious stone and glass
Brand Name:
MAGPOW
Model Number:
SK-1698
SK-1698:
Glass Compound Adhesive
Material:
modified epoxy adhesive
Components rate:
A:B=2:1
Appearance:
yellowing
Feature:
high boding strength
Packing:
3kg/set,6sets/carton
Packaging & Delivery
Packaging Details
common export packing
3kg/set,6sets/carton
Delivery Time
5 days to 30 days after get deposit

Glass Compound Adhesive (SK-1698)

 

[Performance Characteristics]

The product is the epoxy resin adhesive, which has advantages of strong adhesion, good yellow-resistance property, abrasion resistance, water resistance, oil resistance, aging resistance, chemical media resistance, colorless transparent adhesive layer and good toughness.

 

[Technical Parameters]

 

 

NO.

  

Item

 

Technical indicators

1

    

Appearance

A

Component A

 

Colorless transparent liquid

 

B

Component B

 

Colorless transparent liquid

 

2

(mPa·s)

(mPa·s)

A

Component A

800~1200

B

Component B

600~1000

3

AB

Adhesive Mixing Ratio (A:B)

21

4

25,min

Pot Life (25,min)

45~60

5

25,h

Preliminary Curing Time (25,h)

4~6

6

-,MPa

Tensile Shear Strength (Steel-Steel, MPa)

≥10

 

[Scope of Application]

 

The product is used for composite bonding for stone and glass.

 

[Method of Application]

1. Remove the oil, dust and other impurities from the surface of composite slabs and keep it dry.

 

2. Mix the adhesive evenly according to the specified proportion and apply it to the bonding surface evenly.

 

3. Stack the plates in one direction to exclude air bubbles; apply uniform pressure to them for 6-8hours; put them into next process in 24 hours.

 

 

4. The adhesive outflow could be cleaned with acetone before it is cured.

 

[Cautions]

1. Adhesive mixing must be even according to the proportion, so as not to affect the application result.

 

2. In order to improve the adhesive strength, the composite surface of glass could be treated by sand blasting, to strengthen the surface adhesion.

 

3. Stone surface treatment chemicals, non-epoxy adhesive and other chemicals must not be spread to or penetrated into the bonding surfaces, in order to avoid chemical reaction with the adhesive, which will affect the adhesive performance and make the adhesive be not cured

 

4. The apparatuses used to take Component A adhesive and Component B adhesive must not be mixed up; the adhesive scratching apparatus should be cleaned with acetone before the adhesive is cured for future use.

 

5. Do not mix up the lids of adhesive, fasten the lids after application and do not eat the adhesive by mistake!

 

6. Because of the different physical, chemical nature of stone, please test the product experimently in advance to avoid errors!

 

 

Package and transportation

1. The product shall be kept in cool, dry and ventilating warehouse. Its service life is 1 year from its production date and may be put into use upon passing the examination after its expiry date.

 

2. The product belongs to general dangerous items. Please keep it away from heat source, fire source, sun burning, and rain during its transportation. Please handle it gently and avoid rolling, bumping, heavy pressing, upside down and side-placing during its transportation and loading.  

 

3. Packing specification: 3 kg/set (6sets/ carton), plastic bottles package; 60 kg/set, plastic drums package.

 

4. Product standard: Q/BUEZ 0262009