Low Cement Refractory Castable(Low Iron)
Low Cement Refractory Castable
Refractory Castable Manufacturer
This is the low cement refractory castable in the above picture,it was packed in 25kg bags,then 40bags in a ton bag.
TK is one of the biggest manufactures for refractory castable in the northern China.Specialized in this area for about 20years.We have advanced production equipment and professional research personnel.Furthermore,we also have complete QCS (Qulity Control System),you can see that in the below photos.TK has the production capacity 10000tons per month, primarily export to INDIA,USA, AUSTRALIA, JAPAN, KOREAetc.
We are the main supplier of most trading company in our city.
Low Cement Refractory Castable adopts submircon powder technology. Micro powder is used as anchoring agent, aluminate cement as coagulation accelerator, some antidetonant and water reducer will also be added in during the production of Low Cement Refractory Castable. Compared with common Refractory Castable, Low Cement Refractory Castable owns the below characteristics:
1. The dosage of cement is low, the content of calcium only accounts for 1/4-1/3 of common Refractory Castable
2. Wter consumption rate during the construction is almost 1/2 or 1/3 of the common Refractory Castable, so the Low Cement Refractory Castable has high density and low porosity.
3. High normal temperature cure property, intensity will be increased after medium temperature and high temperature. Three or five times more than common Refractory Castable.
4. Good volume stability under high temperature.
Permanent linear change after buring 3h in 1350°c
Cold Crushing Strength after 110°c dried (Mpa)
Modulus of Rupture after 110°c dried(Mpa)
|Thermal shock resistance (times)(900°c water cooling)||≥25|
|Max Working Temp.||1500°c|