A mixture of polymers, organic compounds, inorganic &organic solvent
Rubber to metal
Rubber adhesive bonding agent
Solids Content by Weight:
Packaging & Delivery
1 kg/barrel 3.5 kg/barrel 20 kg/barrel
10-30 days after deposit and confirmed all order
1.Rubber adhesive bonding agent
2.Instead of chemlok topcoat
4.Widely used in rubber to metal
Rubber adhesive bonding agent to metal Topcoat Usage:
General double-coated type rubber to metal heat curing adhesive- Topcoat
1.Bonds a wide variety of rubbers such as: nitrile,Neoprene,Natural rubbers, Butadiene SBR,
Isoprene ,Polybutadiene rubber to metals coated ICM-810
2.Non-toxic, easy to apply: can be applied to metal parts in a variety of ways, including:dip, spray,brush,or roller
3.Excellent environmental resistance: provides superior resistance to heat, water, salt spray, chemicals, oils,solvents, and corrosive atmospheres.
4.Strength bonding, durability, good stability
Rubber op metaal lijm
Composition: A mixture of polymers, organic compounds, inorganic filler and organic solvent Appearance: Black Liquid Solids Content by Weigh: 23~26% Viscosity: (25°C Brookfield,LV-2@30rpm)150~350cps Flash point: 27 °C Diluent: Xylene Solvent: Xylene Shelf Life:24 months(25 °C)in original, unopened container.
Surface treatment: degreaseafter sandblasting processing, or chemical treatment for removing oil, rust, oxide in the surface.coating CISCA-810 in the first as the instructions of CISCA-810, then dry . Mixing:Agitate sufficientlyduring use to keep dispersed solids uniformly suspended. Use a high speed propeller type agitator or the agitator supplied with the drum fully stirred before gluing, use it after evenly mixing, to ensure that the components are evenly dispersed
Dilute: Use as received, or add appropriate amount of dilution .dilution as your usage, diluted products can’t be storaged for a long time.
Brush: not dilution(Use as received)
Dip:add 10%~15% Xylene Spray :Add 50% Xylene Coating:Coating by brush, roller, dipping, spraying and other methods. Paint-coat should be uniform and avoid excessive overflow, (15-20 μ dry film) Drying:It needs about 45-60 minutes to dry at room temperature; The drying time can be cut in heating.
Storage:This product must be stored in dry and normal temperature environment, avoiding to exposure at high humidity and high temperature environment for a long time.
Cleanup :Solvents such as xylene have been shown to work well before heat is applied. Once cured,it cannot be removed by solvent.
Vulcanizing:The adhesive properties will be better in curing rubber and adhesive together. When gumming member are placed in a mold that should be quickly filled rubber tocuring with mold.Recommended: curing temperature 145 ~ 185 °C, curing time 5 ~ 60 minutes, curing pressure as received.
1. Please cover closed the container after using. Because the solvent is volatile.
2.Solvent vapor is harmful, please keep away from fire and keep ventilation in workshop, and prevent inhalation or touch with skin for long-term.
ICM is a high-tech company which sets environment-friendly product and chemicals R&D, production, marketing, and after-sales services as one. With advanced automated production equipment and scientific testing methods.