Part A: 20kg or 180kg
Part B: 2kg or 18kg
310ml Tube per pc, 25pcs per caton Size: 265mm*260mm*260mm=0.018cbm 38500pcs per 20ft container, 1375pcs per CBM
For other detail packing information please contact us we have detail data.
Samples:3 days Standard order:7-10days Other:depend on quantity
1.We are factory best solution for you
3.High stability -60 to +260degree
5.Lowest price 1.5-3.8
Properties before curing
Colorless viscous liquid
Colorless viscous liquid
A:B = 100:100
Viscosity after mixing,mPa·s(25°C)
Operation time after mixing, min(25°C)
Curing addition, min,25°C
25°C/24hr or 80°C/60min or 100°C/ 30mins
Properties after curing
Colorless transparent elastomer
Hardness, Shore A
Tensile strength, MPa
Tear strength, N/mm
Application temperature, °C
- 60 to 260
Two component silicone sealantSI3630 A/B
Detailed Product Description
SI3630A/B is two component RTV addition type silicone sealant. The curing will be faster if heating, the highest heating temperature is 150°C.
1.Easy to cure, 30min in 100°C
2.Excellent mechanical property and dimensional stability
3.Simple application, Speedy mixed by 10:1. The strength and hardness can be adjusted by change the amount of curing agent.
4.High hardness, low curing shrinkage, < 0.2 %
1.Use in duplicate of sample plate, prototype, electronic component, construction and furniture parts.
2.Also use to rolling over of polyurethane foam products, making of rubber roll and nozzle.
3.Use to make adhesive layer of lace ribbon climbing clothes.
1. Mix Part A and Part B by 100:10,The two parts can be mixed by hand work or pneumatic pump, try best to avoid the bubbles and temperature rising.
2. Pouring, the mixed sealant should be degassing by vacuum 30-50 mbar for removing the wrapped bubbles. If using dispersion equipment, the two parts need to be degassing separately before mixing.
The volume will expand to 3-4times while the mixed sealant degassing, then shatter, it will recover after 5-10mins.
The materials may influence the curing:
1. Natural rubber which is vulcanized by sulfur
2. Silicone rubber which is catalytic by metal salt like Sn salt
3. PVC which is made with Sn salt and additive
4. Epoxy resin which is catalytic by amine
5. Some organic solvent, such as Ketone, alcohol, ether etc.
Package and Storage
Part A: 20kg or 180kg Part B needs to be sealed and avoid light and hot
Part B: 2kg or 18kg Shipped and stored as normal chemicals
Shelf life: 12 months(25°C)
Thanks for your visit our website , we are manufacture Polyurethane, Epoxy, Silicone adhesive sealant and grease for automibile ,construction,electronic,ect.
We have the owen factory, Technical team and After service team. We have supplier for many Top 500 company and also OEM for many big brand.
We will provide the professional solution for you.
Out standing customer care services at any time,24 Hour Help Support on line or call +86-400-882-1323
Shanghai Sepuna Chemical Co.,Ltd is a subcompany of PUNADE INTERNATIONAL GROUP, Sepuna is a professional industry adhesive supplier ,manufacturing polyurethane/silicon/epoxy sealant and adhesive,has nearly 10 years history.
In 2005 Sepuna introduced PUNADE technology from Switzerland.
Via the ISO90001:2000 certification.
In 2013 Sepuna introduce Drawing Machine technology and has put it into producing formally now.
Sepuna has professional factory which area is 5.000 squ...