clear silicone rubber for fire resisting sleeves (LSR1318)

FOB Reference Price:Get Latest Price
US $4-7 / Kilogram | 200 Kilogram/Kilograms (Min. Order)
Supply Ability:
300 Ton/Tons per Month
Port:
shanghai
Overview
Quick Details
Place of Origin:
Shanghai, China (Mainland)
Classification:
Double Components Adhesives
Main Raw Material:
Silicone
Usage:
Fiber & Garment, fiberglass sleeving
Brand Name:
Jorle
Model Number:
LSR1318
Density(g/cm3):
1.15
Curing Time (180°C,min):
10
Tensile Strength (Mpa):
≥3.0
Hardness(shore A):
39±4
Tearing Strength (KN/m):
≥15
water absorption:
0.01-0.02 24h,25°C,%
Curing Time (25°C,h):
24
Elongation Break(%):
≥300
Operation Time (25°C,min):
48
Ratio(weight ratio,A:B):
100:2
Packaging & Delivery
Packaging Details:
clear silicone rubber for fire resisting sleeves (LSR1318)
Agent A: 20kg, Agent B: 1kg
Delivery Detail:
3-5 working days

Specifications

clear silicone rubber for fire resisting sleeves (LSR1318)
1.good release
2.low linear shrinkage
3.good chemical stabiliy

clear silicone rubber for fire resisting sleeves (LSR1318)

Product Description:

clear silicone rubber for fire resisting sleeves (LSR1318)

This product is made of high temperature curing two-component addition type liquid silicone rubber, designed specifically for precision mold fabrication, and fiber glass sleeving coating. After curing have the dimensional stability, good release properties, tear-resistant high strength, low linear shrinkage, excellent ozone and UV aging resistance, non-toxic, tasteless, and has good biocompatibility. This product is easy to use, compound viscosity is moderate, high temperatures can be quickly cured.

 

Characteristics after curing:

clear silicone rubber for fire resisting sleeves (LSR1318)

1. Quick curing at high temperature, easy to use;

2. Addition-curing, does not release any gases;

3. Superior mechanical properties, low linear shrinkage;

4. Excellent ozone and ultraviolet resistance;

5. Excellent electrical properties, good chemical stability;

6. Moisture-proof, waterproof, resistant to ozone, weather-resistant.

 

Typical Properties:

 

Testing Item

Testing standard

Unit

A

B

Outside view

visual inspection

---

clear viscous liquid

clear viscous liquid

viscosity

GB/T 10247-2008

mPa·s(25°C)

50000

500±150

density

GB/T 13354-92

g/cm3(25°C)

1.10

0.99

 

Typical performance:

 

Testing item

Testing standard

Unit

Value

hardness

GB/T 531.1-2008

Shore A

39±4

elongation at break

GB/T 528-1998

%

200

Tensile Strength

GB/T 528-1998

Mpa

3.0

conductivity factor

GB/T 10297-1998

W/mK

0.17

expansion coefficient

GB/T 20673-2006

μm/(m,°C)

210

water absorption

GB/T 8810-2005

24h,25°C,%

0.01-0.02

tear strength

GBT 529-2008

kN/m

20

dielectric strength

GB/T 1693-2007

kV/mm(25°C)

>18[

loss factor

GB/T 1693-2007

(1MHz)(25°C)

0.001

dielectric constant

GB/T 1693-2007

(1MHz)(25°C)

0.33

volume resistance

GB/T 1692-92

(DC500V)Ω· cm

1.2×1015

 

Packing:

Agent A: 20kg, Agent B: 1kg

 

Storage And Transport:

1. Cool dry place for storage, storage period for 1 year. (25°C)

2. This product is non-dangerous goods, according to the General chemical transportation.

3. Colloidal components A and B shall be sealed, and care during transport leaked.

4. Over shelf products should confirm that there is no exception before use.