epikote pouring sealant for electronic

FOB Reference Price:Get Latest Price
US $4-7 / Kilogram | 200 Kilogram/Kilograms epikote pouring sealant for electronic (Min. Order)
Supply Ability:
30 Ton/Tons per Month epikote pouring sealant for electronic
Port:
Shanghai
Overview
Quick Details
Place of Origin:
Shanghai, China (Mainland)
Classification:
Double Components Adhesives
Main Raw Material:
Epoxy
Usage:
Construction, Electronics
Brand Name:
Jorle
Model Number:
ZR611
hardness:
80 Shore D
Mixed viscosity:
paste mPas(25°C)
water absorption:
<0.1 24h 25℃ %
dielectric strength:
>20 kV/mm 25℃
conductivity factor:
0.4 W/mK
expansion coefficient:
44 μm/(m,℃)
Mixture density:
1.50 g/cm3(25°C)
operation time:
40 min 25℃
Loss factor:
0.014 (1MHz)(25℃)
curing time:
80/1.5 or 25/10 ℃/hr
Packaging & Delivery
Packaging Details
20 kg /set; 5kg / set
We can also packing epikote pouring sealant for electronic as your requirement.
Delivery Time
Within 25-30 days upon receipt of your L/C or 30% deposit

Specifications

epikote pouring sealant for electronic is one of our most popular products.Against moisture, dirt and other atmospheric......

epikote pouring sealant for electronic       

 

Description:

ZR611 epikote pouring sealant for electronic is a room temperature/heating curing epoxy resin glue. ZR611 is used for design, protection of the potting need high strength or confidential electronic products.

ZR611 epikote pouring sealant for electronic without heating can cure. 1:1 (weight ratio) completely mixed part A and part B, form protection in a period of curing time.

 

After curing glue has the following characteristics:

Against moisture, dirt and other atmospheric composition

High strength

Has confidential role   

Solvents, no cure by-products

Fireproof performance

Have stable mechanical and electrical properties between -45°C-120°C

 

Conventional performance:

 

test item

testing standard

unit

A

B

Outside view

visual inspection

---

black viscous liquid

yellow viscous liquid

viscosity

GB/10247-2008

mPa·s(25°C)

paste

paste

density

GB/T 13354-92

g/cm3(25°C)

1.60

1.40

 

Operation process:

 

test item

unit

value

mixture ratio

weight ratio

1:1

mixture ratio

volume ratio

100:125

Mixed viscosity

mPa·s(25°C)

paste

Mixture density

g/cm3(25°C)

1.50

operation time

min(25°C)

40

curing time

°C/hr

80/1.5 or 25/10

Operation time is a quantity of cement with 100 g.

 

A, B two components in proportion to remove mixing ratio, mixing, vacuum suction bubble in operation period, remove the potting products to casting, such as potting product is too big, suggest points potting, then according to The Times curing(80°C/90min or 25°C/10hr)

 

Operation caution:

Agent A place for a long time, maybe produce precipitation, mix part A and B access should be paid attention to save after sealing.

Mixing should pay attention to the same direction, otherwise, it will stir with too much bubble; Borders and the bottom of the container sizing material should also stir well, can appear otherwise stir caused by uneven local not curing phenomenon.

Casting the product vacuum pumping, remove again bubble can improve after curing products comprehensive performance.

Temperature is too low will lead to curing speed partial slow, heat cure advice; Potting thickness more than 2 cm above 80 °C not directly in the curing, lest cause explosive together.

This glue curing exothermic reaction, match the process as the quantity of cement can affect the operation, so the length of time with 100 g resin content of operation time is only a reference time.

 

Typical performance:

 

test item

testing standard

Unit

value

hardness

GB/T 531.1-2008

Shore D

80

conductivity factor

GB/T 10297-1998

W/mK

0.4

expansion coefficient

GB/T 20673-2006

μm/(m,°C)

44

water absorption

GB/T 8810-2005

24h,25°C,%

<0.1

dielectric strength

GB/T 1693-2007

kV/mm(25°C)

>20

Loss factor

GB/T 1693-2007

(1MHz)(25°C)

0.014

dielectric constant

GB/T 1693-2007

(1MHz)(25°C)

3.53

volume resistance

GB/T 1692-92

(DC500V)Ω· cm

1.2×1015

Remark:All the above data come from 25 °C and 55% RH glue curing conditions after 7 days.

 

 

Packing:

 

20 kg /set; 5kg / set

 

Storage and transportation:

Part A and part B need to avoid light, heat, save after sealed. (Can be used as the non-dangerous goods transport and storage)

Shelf life Agent A: 1 year, Agent B: 6 months(25°C)