jorle epoxy resin for electronic potting

FOB Reference Price:Get Latest Price
500 Kilogram/Kilograms jorle epoxy resin for electronic potting (Min. Order)
Supply Ability:
500 Ton/Tons per Month jorle epoxy resin for electronic potting
Port:
shanghai, ningbo
Seller Support:
Payment protection
On-time shipment
Product quality protection
Payment:
More
Overview
Specifications
Place of Origin:
Shanghai, China (Mainland)
Classification:
Double Components Adhesives
Main Raw Material:
Silicone
Usage:
electronics
Brand Name:
Jorle
Model Number:
ZR6109
hardness:
Shore D
glass transition temperature:
160 DSC °C
water absorption:
<0.1 24h,25°C,%
dielectric strength:
>20kV/mm(25°C)
Loss factor:
0.014(1MHz)(25°C)
curing time:
80/1.5 or 25/10 °C/hr
dielectric constant:
3.53 (1MHz)(25°C)
operation time:
30 25°C,min
Mixture density:
1.15 25°C,g/cm3
Mixed viscosity:
1000-2000 25°C,mPa*s
Packaging & Delivery
Packaging Details:
jorle epoxy resin for electronic potting as your requirement to pack
Delivery Detail:
10-15 working days

Specifications

jorle epoxy resin for electronic potting
1. high temperature resistant
2. resistance to cracking
3. No solvents

electrical epoxy resin for encapsulation

 

Description:

ZR6109 jorle epoxy resin for electronic potting is a kind of room temperature/heating cured epoxy resin glue. This kind of two-component epoxy adhesive design for bonding ceramics, the metal, glass, plastic, rubber, paper, cloth, etc.


ZR6109 jorle epoxy resin for electronic potting without heating can cure. To 4: 1 (weight ratio or the volume in the mixture thoroughly A part A and part B, curing in a certain time, and form protection.

 

Characteristics: 

1. Good toughness and hardness
2. Room temp curing, high temperature resistant
3. Excellent bonding, resistance to cracking
4. Good sealing performance
5. No solvents, no cure by-products
6. Have stable mechanical and electrical properties between -45&deg; C-150&deg; C

 

A, B two components in proportion to remove mixing ratio, mixing, vacuum suction bubble in operation period, remove the potting products to casting, such as potting product is too big, suggest points potting, then according to The Times curing(80&ordm;C/90min or 25&ordm;C/24hr)

 

Conventional performance:

 

test item

testing standard

unit

A

B

Outside view

visual inspection

---

Light yellow liquid

yellow liquid

viscosity

GB/10247-2008

25°C,mPa·s

10000-20000

50-100

density

GB/T 13354-92

25°C,g/cm3

1.15

1.15

 

 

 

 

Operation process:

 

 

test item

unit

value

mixture ratio

weight ratio

100:25

mixture ratio

volume ratio

100:25

Mixed viscosity

25°C,mPa·s

1000-2000

Mixture density

25°C,g/cm3

1.15

operation time

25°C,min

30

curing time

°C/hr

80/1.5 or 25/10

                              Operation time is a quantity of cement with 100 g.

 

 

Typical performance:

 

 

test item

testing standard

Unit

value

test item

GB/T 531.1-2008

Shore D

80

hardness

GB/T 20673-2006

μm/(m,°C)

44

expansion coefficient

GB/T 8810-2005

24h,25°C,%

<0.1

water absorption

GB/T22567-2008

DSC °C

160

glass transition temperature

GB/T 1693-2007

kV/mm(25°C)

>20

dielectric strength

GB/T 1693-2007

(1MHz)(25°C)

0.014

Loss factor

GB/T 1693-2007

(1MHz)(25°C)

3.53

dielectric constant

GB/T 1692-92

(DC500V)Ω· cm

1.2×1015

                   Remark:All the above data come from 25 °C and 55% RH glue curing conditions after 7 days.

 

 

Operation caution:

 


1. Agent A place for a long time, maybe produce precipitation, mix part A and B access should be paid attention to save after sealing.

 
2. Mixing should pay attention to the same direction, otherwise, it will stir with too much bubble; Borders and the bottom of the container sizing material should also stir well, can appear otherwise stir caused by uneven local not curing phenomenon.

 


3. Casting the product vacuum pumping, remove again bubble can improve after curing products comprehensive performance.

 


4. This glue curing exothermic reaction, match the process as the quantity of cement can affect the operation, so the length of time with 100 g resin content of operation time is only a reference time.

 

Packing:


5kg/ set

 

Storage and transportation:

 


1. Part A and part B need to avoid light, heat, save after sealed. (Can be used as the non-dangerous goods transport and storage)
2. Shelf life Agent A: 1 year, Agent B: 6 months (25&ordm;C).

 

 

 

Transaction History of the Supplier

Below is the information about the supplier's transactions conducted via Alibaba.com. If you require further details regarding the transaction data, please contact the supplier directly.

Transaction Overview

Transactions

Transaction Details

This supplier has completedtransactions with buyers from .

Shipping Destination
Transaction Value
Transaction Date

Send your message to this supplier

Not exactly what you want? 1 request, multiple quotations Get Quotations Now >>
You May Like:
aisn-detail010176215073