Low-iron silver mirror
See larger image: Low-iron silver mirror
Supplier Details
Beijing Northglass Sunny Glass Co., Ltd.
- Business Type:Manufacturer, Trading Company, Distributor/Wholesaler
- Product/Services:Low-iron glass,copper-free mirror,silk screen printed glass,decorative ...
Product Details
A mirror that could stay 10 times longer than the conventional mirror.
It is an innovative production. Endless pursuit leads to perfection.
Perfect from the nature and the Unmatched
Copper is normally the coating material in conventional mirrors. It is easily be oxidized due to the changing of temperature, humidity and salt in the air causing defects like edge corrosion, black spots and cloud. Images become easily blurred.
Perfect from the Preservation
Imported the Bonove production facility from Europe, incorporates with the worlds latest environmentally friendly copper free mirror production technology. The production process not only complies with but far exceeds the international environmental protection standard.
Perfect from the Healthy
Having worked closely with Valspar, the worlds renowned solution provider with 200 years expertise, MirroRex has been successfully created, with outruns all of the competitors in the market. With its patented solution, MirroRex becomes much more durable and performs better than others.
We always believe that quality control is more important than production speed. It is particularly important where heat and humidity violate the stability of the silver coating. Therefore, the environment of the production workplace is under severe control to ensure every piece of MirroRex is produced in dustless, dry and fixed temperature environment.
Technical Parameters
| Accelerated Testing Compare with Other Mirrors | |||
| European Norm EN1036 | Typical Conventional Mirror | MirroRex Copper Free Mirror | |
| ISO 3768 CASS Test @120 Hours | |||
| Maximum Edge Corrosion (um) | 2500 | 500-1000 | 250 |
| Spot Failtures-numbers/sq dm. | 2<3mm | 3 | <=1 |
| 3<0.3mm | |||
| ISO 3770 Salt Test @ 5% | |||
| Maximum Edge Corrosion (um) | 1500 | 300 | 100 |
| Spot Failtures-numbers/sq dm. | 2<3mm | 1 | <=1 |
| 5<0.3mm | |||
| ASTM C 1503-01 Salt Spray Test - 20% US Spec for 300 Hours | |||
| Maximum Edge Corrosion (um) | 3000 | 500 | 200 |
| Spot Failtures-numbers/sq dm. | 2<3mm | 1 | 1 |
| 5<0.5mm | |||
| Max. Numbers of Spot Failures | 5 | ||
| DIN 50017 Humidity Test - 480 Hours | |||
| Maximum Edge Corrosion (um) | 200 | 0 | 0 |
| Appearance | No clouding of silver film | Clouding occurs in 3-4 days | No clouding of silver film |
| Ammonia Immersion (10%) - 240 Hours | No standard established | Paint delaminates in 3-5 hours | No paint delamination 10 days |
| Typical Edge Failure-2 Hours(um) | 250 | 200 | <50 |
| Heat Test @ 160 Degrees F (71C) | No standard | Severe clouding after 4 hours | No clouding after 10 days |
| Heat Test @ 425 Degrees F (218C) | No standard | Severe clouding after 30 minutes | No clouding after 10 hours |