Low Smoke Free of Halogen SILANE XLPE CrossLinking Polyolefin lszh Compound

FOB Reference Price:Get Latest Price
$6.00 - $8.00 / Kilograms | 25 Kilogram/Kilograms (Min. Order)
Report Suspicious Activity
Overview
Quick Details
Place of Origin:
Taiwan, China
Brand Name:
GYC
Model Number:
GY-SL-5001
Density:
1.45
Tensile Strength:
13 MPA
Elongation at Break:
175 %
HCI and HBr content:
0 mg/g
Supply Ability
Supply Ability:
20000 Kilogram/Kilograms per Month
Packaging & Delivery
Packaging Details
25Kg/bag, Stored at cool place away from direct sunlight.
Port
Kaohsiung
Lead Time :
Within 7 Days
Product Description

LSFOH Polyolefin Compound


GY-SL-5001 belongs to silane cross-liking low smoke flame retardant polyolefin compound (lszh compound) without halogen. It is a combination of Halogen-free masterbatch and silane XLPE. GY-SL-5001 features excellent electrical performance, physical properties, stability and can be applied to low-voltage wire & cable insulation and sheathing. 

Properties
Item
Spec.
Value
Density
-
1.45
g/cm3
Tensile Strength
≧10
13
MPa
Elongation at Break
≧150
175
%
Heat elongation (200℃ x 15min x 0.2MPa)
Maximum elongation change under load
≦100
85
%
Maximum permanent elongation change after cooled
≦25
5
%
Volume resistance (20℃)
≧1 x 1012
1.5 x 1013
Ω.m
Volume resistance (90℃)
≧2 x 108
1.5 x 109
Ω.m
Oxygen index
≧30
32
%
HCI and HBr content
≦0.5
0
mg/g
HF content
≦0.1
0
mg/g
Suggested Methods

1. Extrusion for most PVC equipment. Processing technique is as following

*Ratio of length and diameter       18-25:1
*Screw diameter                              45-120 minutes
*Compressing Ratio                        1.5-2.5
*Filtering mesh                                 40/60/40


2. Processing Temperature

Feeding Zone
Compression Zone
Metering Zone
Neck
Die
110-120℃
120-130℃
130-140℃
140-150℃
140-150℃

3. Crosslinking
- Extruded cables can be fast crosslinked when bathed in 80-90℃ hot water.
- Low pressure steam bath at 80-90℃ can help crosslinking, too.
- Avoid overly high temperature to prevent from adhesion.
- The crosslinking time depends on the thickness of the insulation layer and size of coil.