Tool steel bar M2 /1.3343 SKH51 SKH9 hss strips m2

Feedback Ratings
$7.10 / Milligram | 100 Milligrams (Min. Order)
Quantity:
- + Milligrams available
0piecesselected, US $in total
View Details
Shipping fee:
Depends on the order quantity.
Lead Time:
15 day(s) after payment received
Contact Supplier
Report Suspicious Activity
Overview
Quick Details
Steel Grade:
M2/DIN1.3343/W6Mo5Cr4V2
Standard:
AISI, ASTM, BS, DIN, GB, JIS
Dimensions:
2.0-200
Place of Origin:
Liaoning, China (Mainland)
Brand Name:
DLDT
Model Number:
M2
Technique:
Hot Rolled
Application:
Tool Steel Bar
Alloy Or Not:
Is Alloy
Special Use:
Cold Heading Steel
Type:
Alloy Steel Bar
Surface:
bright and black Tool Steel hss strips m2

Packaging & Delivery

Selling Units:
Single item
Single package size: 
3000X300X300 cm
Single gross weight:
150.0 kg
Package Type:
wooden case
Picture Example:
package-img
package-img
Lead Time :
15

 High Speed Tool Steel M2 / 1.3343 / SKH51

 

China

Japan

 USA

Germany

Application

W6Mo5Cr4V2

SKH51

 M2

1.3343

 Suitable for making high -speed cutting tools, various kinds of drills, broaches, milling cutters.High-speed precise mould and press mould.

 

Chemical composition (%)

Grade

C

Si

Mn

P

S

Cr

Mo

W

V

1.3343

0.86-0.94

≤0.45

≤0.40

≤0.030

≤0.030

3.80-4.50

4.70-5.20

5.90-6.70

1.70-2.10

M2

0.78-0.88

0.20-0.45

0.15-0.40

≤0.030

≤0.030

3.75-4.50

4.50-5.50

5.50-6.75

1.75-2.20

W6Mo5Cr4V2

0.80-0.90

0.20-0.45

0.15-0.40

≤0.030

≤0.030

3.80-4.40

4.50-5.50

5.50-6.75

1.75-2.20

 

 

 

 

 

 

 

 

 

  Tool Steel hss strips m2

Product Description

M2 high speed steel round bars
To meet end users further processing needs, the material what we provided is without heat-treatment.

Our hss materials sold to foreign and domestic market. We have own plant and have reliable professional supplie
package for bars:
the bars will be oiled for rust protection, - one dia should be packed in one bundle by the steel strip; bundles should be oiled and turned into the PE film then packed in wooden boxes for easy loading.

Tungsten molybdenum high speed steel M2
HSS M2 has a series of advantages, like small carbide and well distributed, higher wear-resistance, and lower cost. the hardness main 57HRC-58 HRC, and 52-53 HRC separately under 500°C-600°C. Bending strength can be 4700MPa, the toughness and thermoplasticity can be improved 50% compare with W18Cr4V, can be used as making different of tools. like drills, screw tap, miller cutter, reamer, knife ect, can be meet normal material request.

Our Services
Provide samples, but need to pay the samples fees, 100RMB/Kg.


M2 is widely used in applications requiring a high degree of toughness; grindability, good wear resistance and high hardness.

Applications include:

-Lathe Tools; Planer Tool;

-Drills; Taps; Reamers; Broaches;

-Milling Cutters; Thread Cutters; End Mills;

-Blanking Dies; Gear Cutter; Router Bits.


Heat Treatment

Forging:

-Preheat slowly to 1600 F until piece is thoroughly heated through, then increase heat to 1950 F -2050 F.

-DO NOT hot work M2 below 1700 F.

- After forging, allow M2 to cool slowly, packed in lime or other insulating material.( For large forgings, let soak in large furnace at 1450 F, then cool in furnace.)

-Anneal as soon as possible.

Anealing:

-Surface protection-Anneal in controlld atmosphere furnace or pack in an inert material.
-Slowly heat M2 to 1550-1600, cool slowly at a rate of 20 F/ hr until furnace is black. Shut down furnace, allow to cool normally, annealed hardness range is 200-240 Brinell.

Stress-relieving:

Temperature 1100-1290 F. Rough machine after stress relieving. Hold tool for 2 hours after reaching full temperature. Cool in furnace to 930 F and then air-cool.

Hardening:

Single-edge cutting tools: 2175-2225 F ( salt bath)
2200 F -2250 F( furnace)

Roating multi-edge cutting tools: 2150 F -2250 F

Punches, dies, etc: 1920-2100 F.

Tempering:

-Temper immediately when piece reaches 150 F or when comfortably hand-held.
-Tempering temperature should be in the range of 1250 F-1100 F.
-Heat slowly to temperature, hold tools at heat for 2 hours before air cooling.
-For best toughness, after tool has cooled, retemper for 2 additional hours at slightly lower temperature.

Tool Steel hss strips m2

Packaging & Shipping

Packing details:

1. wrapping clothes is suitable for shipping

2. in wooden case

3. the good's quantity in each case is no more than 4 tons

 

Company Information

Helpful hints

AISI M2 M35 T1 (DIN 1.3343 1.3243 1.3355)steelHot rolled steel bar) product is our company the most outstanding advantage flagship product using a variety of detection means To ensure the good quality to adopt the latest production technology and equipment Make the production cycle shorten order quantity in the 1000 kg or more to ensure rapid delivery of the goods in the 15 to 20 days

Processing

 

  Tool Steel hss strips m2

Our Services

Qualified inspection,adopting advanced technology and equipment to test products internal cracks and pores to ensure that the internal structures are good.

Do the test to confirm the material chemical composition.To make the material conform to the requirements of the relative models in corresponding fields.

 

FAQ

1.What’s the MOQ for your HSS products?

---It’s100kg. 

2.Delivery time?    

---25-35 days   

3.What’s the Payment term?

--- T/T or L/C    

 

Buying Guides

the size is smaller, the price will be higher between 375usd to 1971 usd.

 

We offer the princip

JingTai industry &trade co., LTD. Dalian friendship prompt:

 

Sold products quotation principle: the producer price shall prevail, additional actual must charge, such as taxes, freight, customs clearance fee and so on, so offer solid confidence, all services are beyond price. Company actual profits by the factory. Namely: if you are the same product to the factory purchasing, to the price of this company is completely consistent, the factory to production as the center and the company for the purpose of service and good let you rest assured.

 

OEM Service

Steel sales the company passed the ISO international quality management system and environmental management system certification.

 

Tool Steel hss strips m2

You May Like
Not exactly what you want? 1 request, multiple quotations Get Quotations Now >>
You May Like