Place of Origin
Henan, China
Refractoriness (Degree)
1770°< Refractoriness< 2000°
Processing Service
Moulding
Application
Industrial Furnaces
Raw material
High Alumina Bauxite
Apparent Porosity, %
22-28
Cold Bending Strength, Mpa, min
30
Refractoriness under Load
1300 (0.2Mpa),℃, min
Working Temperature ℃ min
1200
Thermal Shock Resistance min
30 cycles